Polyester TPU

You are welcomed to come to our factory to buy the latest selling, low price, and high-quality Polyester TPU. Zhongsu look forward to cooperating with you.

Send Inquiry

Product Description

Polyester TPU

Zhongsu high quailty Polyester TPU is widely used in IT, wearable, wire and cable, automobile, smart home and other industries based on its excellent wear resistance, tensile resistance, heat resistance, winding resistance, good elasticity and high cost performance.

Polyester TPU is widely used in IT, wearable, wire and cable, automobile, smart home and other industries based on its excellent wear resistance, tensile resistance, heat resistance, winding resistance, good elasticity and high cost performance.

Polyester injection molding:

Injection molding, also known as injection molding, is a molding method of injection and molding. It has fast production speed, high efficiency and automatic operation. The size can be from large to small and the size is accurate. It can form parts with complex shapes. It is suitable for the molding and processing fields of large star production and complex products.

Polyester extrusion:

In plastic processing, it is also called extrusion molding or extrusion. It refers to a processing method in which the material passes through the action between the extruder barrel and the screw, while being heated and plasticized, and is pushed forward by the screw, and continuously passes through the head to make various cross-section products or semi-finished products.

Project	Unit	Type Value
Polyester TPU
Hardness	Shore-A/D	55A	60A	65A	70A	75A	80A	85A	90A	95A	55D	65D	75D	85D
Specific Gravity	g/cm3	1.16	1.17	1.17	1.18	1.18	1.19	1.19	1.19	1.2	1.21	1.21	1.22	1.22
Tensile strength	MPa	15	17	22	25	32	35	40	45	50	52	55	60	60
Tensile modulus 100%	MPa	2.7	3.2	3.5	3.8	4.5	5	7	10	15	16	22	35	35
Tensile modulus 300%	MPa	4	4.5	5.5	7	8.5	12	15	24	35	38	40	43	43
Elongation at break	%	850	830	750	650	600	550	500	450	400	380	350	300	300
Tear strength	KN/mm	62	70	75	80	85	92	103	110	120	125	150	165	200
Abrasion quantity	mm3	～	～	110	97	95	90	75	65	60	56	50	45	45
Recommended melting temperature		Drying time				Drying temperature				The values in the table represent typical values only, not absolute values.
160-220℃		3H-4H				90-100℃